A Bi-doped RuO₂ catalyst for efficient and durable acidic water oxidation

iridium oxide (IrO₂), which can suffer from highly oxidative and corrosive conditions, has been regarded as the state-of-the-art anode catalyst for PEMWE. However, the high cost associated with low mass activity strictly hinders the scale-up utilization.

Therefore, designing and exploring cost-effective catalysts with high electrocatalytic performance and stability toward acidic OER are of great urgency but still remain challenging.

Recently, ruthenium oxide (RuO₂) is regarded as a promising alternative to IrO₂ for acidic OER due to its high intrinsic activity and low price.

It is known that increasing the initial oxidation state of Ru in RuO₂ to promote active Ru-centered oxidation is an effective strategy to enhance the electrocatalytic performance. To this end, great efforts have been devoted to doping foreign elements to adjust the valance state of Ru in RuO₂-based catalysts, leading to much-enhanced activity.

However, the easy overoxidation of Ru sites to form soluble RuO₄^2- species at high potential during the process of OER usually results in the collapse of crystal structure and dissolution of Ru species, which is the very reason for the unsatisfied long-term stability of RuO₂ for acidic OER.

Thus, developing an efficient strategy to balance the seesaw relation between stability and activity of RuO₂-based catalysts is essential for the practical application of PEMWE, yet challenging.

Recently, a research team led by Prof. Wei Luo from Wuhan University, China, developed a modified RuO₂ catalyst with bismuth (Bi) doping (Bi_0.15Ru_0.85O₂) to simultaneously boost the activity and stability toward acidic OER. X-ray photoelectron spectroscopy (XPS) and Ru L_2,3-edges X-ray absorption near-edge structure (XANES) spectra demonstrate the increased initial oxidation state of Ru in Bi_0.15Ru_0.85O₂ after Bi doping.

Electrochemical experiments, ultraviolet photoemission spectroscopy (UPS), and ultraviolet-visible spectroscopy (UV) spectra characterizations indicated reveal much faster electron transfer and better electroconductibility in Bi_0.15Ru_0.85O₂.

Apparent activation energy tests and density functional theory (DFT) calculation results suggest the introduction of Bi can effectively reduce both the apparent activation energy and energy barrier of the rate-determining step from O* to OOH*, thereby leading to much-enhanced activity, with a low overpotential of 200.0 mV at 10 mA cm^-2, as well as long-term stability over 100 hours.

The findings are published in the Chinese Journal of Catalysis.

More information:
Liqing Wu et al, A Bi-doped RuO₂ catalyst for efficient and durable acidic water oxidation, Chinese Journal of Catalysis (2023). DOI: 10.1016/S1872-2067(23)64554-1